Orient manufacturers a wide variety of Conventional and Low Cement Castables based on all types of Aluminous raw materials.

Conventional Castable

	Max. Service Temperature	Grading mm	PLC (%) 1550oC 2 Hrs.	Setting	CCS Kg/Cm2 Min.110 0C	Al203% Min.	Fe203% Max.	Ca0% Max.
ORCAST- 97S	1850	0-5	±0.50	Hydraulic	700	97.00	0.30	2.80
ORCAST-95S	1800	0-5	± 1.00	Hydraulic	500	94.00	0.30	3.50
ORCAST-90SD	1700	0-5	± 1.00	Hydraulic	650	88.00	0.70	5.80
ORCAST-90S	1750	0-5	± 1.00	Hydraulic	550	90.00	0.80	4.80
ORCAST-80S	1650	0-5	± 1.00	Hydraulic	500	80.00	1.00	4.80
ORCAST-70S	1650	0-5	± 1.00	Hydraulic	500	70.00	1.00	4.80
ORCAST-60SD	1600	0-5	± 1.50	Hydraulic	450	60.00	1.00	5.80
ORCAST-60S	1600	0-5	±1.50	Hydraulic	350	60.00	1.00	4.80
ORCAST-50SD	1500	0-5	±1.50*	Hydraulic	450	50.00	1.30	5.80
ORCAST-50S	1500	0-5	±1.50*	Hydraulic	350	50.00	1.30	4.80
ORCAST-70N	1450	0-5	±1.50**	Hydraulic	350	72.00	4.50	10.00

* PLC at 1500oC/ 2 hours
** PLC at 1450oC/ 2 hours


Low Cement Castable

Prod uct	Max Serv ice Tem poC	Grad ing (mm)	Water (%)	B.D. (gm/ cc)	PLC% 1400oC / 3 hrs	CCS Kg/ cm 2				Al2O3 Min %	Fe2O3 Max %	CaO Max %
						110oC / 24 hrs	800oC / 3 hrs	1250 oC / 3hrs	1500oC / 3hrs
LCC 45	1500	0-6	6-6.5	2.3	+/- 1.0	600	700	800	1000	45	1.2	2.2
LCC 60	1600	0-6	6-6.5	2.55	+/- 0.8	650	750	850	1000	60	1.0	2.0
LCC 70	1650	0-6	4-4.5	2.8	+/- 0.5	700	800	900	1100	70	1.0	1.6
LCC 70 (Mullite)	1750	0-5	4-4.5	2.8	+/- 0.5	700	800	900	1100	70	0.5	1.5
LCC 80	1700	0-5	4-4.5	2.85	+/- 0.5	800	800	1000	1200	80	1.0
LCC 90 BR	1750	0-5	4-4.5	2.90	+/- 0.5	900	900	1000	1250	90	0.5	1.5
LCC 95 W	1800	0-5	4-4.5	2.90	+/- 0.4	1000	1000	1100	1300	90	0.3	1.5

Blast Furnace Trough Castable

Trough castables and rocking runners are employed on the casthouse floor to transfer molten iron tapped from blast furnace to torpedo cars. The Company manufacturers gel bonded (cement Free) castables containing Silicon Carbide.